MAPEFILL GP
Low Embodied Carbon
Sustainable Manufacturing Process
Colour | : | Grey |
Usage | : | Interior | Exterior |
Flooring | : | Flooring |
Material | : | Concrete |
Characteristics | : | Total absence of shrinkage in the plastic (ASTM C827) and hardened phase, and develops early flexural and compressive strength |
Consistency | : | Powder |
Weight | : | 25,25 kg ,kg |
Maximium aggregate size | : | 1 mm |
Bulk density | : | 1300 kg/m3 |
Dry solid content | : | 100 % |
Chloride ions content | : | ≤ 0.05% |
Colour of mix | : | Grey |
Trowel mix ratio | : | 25 kg of Mapefill GP with 3.25-3.75 litres of water |
Pourable mix ratio | : | 25 kg of Mapefill GP with 3.75-4.25 litres of water |
Flowable mix ratio | : | 25 kg of Mapefill GP with 4.25-4.75 litres of water |
Consistency of mix: | : | Fluid (using 19% of water) |
Flow | : | < 60 sec. (using 19% of water) |
Density of mix | : | 2200 kg/m3 |
pH of the mix | : | > 11.5 |
Application temperature range | : | From +5°C to +40°C |
Pot life of mix | : | 60 minutes |
Initial setting time | : | 7 hr |
Final setting time | : | 8 hr |
Compressive strength | : | > 5 MPa (after 1 day) | > 7 MPa (after 7 days) | > 8 MPa (after 28 days) |
Bleeding | : | Absent |
Volume expansion | : | 1.0% |
Drawing resistance of steel rods - displacement at 75 kN load | : | ≤ 0.6 mm |
Reaction to fire | : | A1 | A1 |