PLANITOP HPC
Low Embodied Carbon
Sustainable Manufacturing Process
Material | : | Concrete |
Colour | : | Grey |
Characteristics | : | A ready-mixed free-flowing mortar made from two components: component A (powder) and component B (HPC Fibres). |
Application | : | Repairing and strengthening of concrete structures that require the use of a free-flowing, ultra-high performance and high ductility mortar without using reinforcing steel in order to limit the thickness applied. |
Colour Of Mix | : | Grey |
Length | : | 13 mm |
Packaging | : | 25 kg bags (component A) | Boxes containing 6.5 kg of Fibre HPC stiff metal fibres (Component B) |
Diameter | : | 0.21 mm |
Consumption | : | Approximately 20 kg/ m² per cm of thickness |
Consistency | : | Powder |
Bulk Density | : | 1.400 kg/ m³ |
Maximum Size Of Aggregate | : | 1.0 mm |
Dry Solids Content | : | 100 % |
Ion Chloride Content - – Minimum Requirement ≤ 0.05% | : | ≤ 0.05 % |
Density Of Material According To EN 14889-1 | : | 7.85 g/ cm³ |
Tensile Strength | : | 2.750 MPa |
Modulus Of Elasticity | : | 200 GPa |
Elongation At Failure | : | 1.5 - 3.0 % |
Mixing Ratio | : | 100 parts by weight of component A (powder) with 6.5 parts by weight of component B (Fibre HPC) (1.625 kg fibres for every 25 kg bag) and 11.5-12.5 parts of water (2.9-3.1 l water for every 25 kg bag) |
Density | : | 2.450 kg/ m³ |
pH Of Mix | : | > 12.5 |
Application Temperature Range | : | +5 °C to +35 °C |
Pot Life Of Mix | : | Approx. 45 minutes (at +20°C) |
Set To Light Foot Traffic | : | 24 h (at +20°C) |
Set To Heavy Foot Traffic | : | 72 h (at +20°C) |
Storage | : | 12 months |