Mapecoat TNS Multisport Professional
Low Embodied Carbon
Sustainable Manufacturing Process
Product type | : | Mapecoat TNS Multisport Comfort,Multi-layered system |
Colour | : | Available in 24 different colours from the standard colour chart and personalised colours upon request |
Material | : | Acrylic resin |
Product size | : | Contact us for more details,Contact us fore more details |
Vapour diffusion resistance coefficient | : | 200 μ |
Change in colour after 1.000 hours exposure to a Weather-Ometer | : | ΔE < 0.8 ΔE < 0.5 |
Elongation at failure after 7 days at ± 23°C | : | 110% |
Ultimate tensile strength after 7 days at ± 23°C | : | 0.7 N/mm2 |
Shore A hardness | : | 60 |
Taber abrasion test after 7 days at +23°C-50% R.H CS17 disk, 1000 revs | : | <0.1 g (<1%) loos by weight |
Wet abrasion | : | > 15.000 cycles |
Viscosity of product | : | 19.000 ± 1.000 mPa.s |
Dry solids content | : | 70% |
Density | : | approx, 1.40 g/cm3 |
Consistency | : | thick liquid |
Resistance to the passage of vapour of a 0.10 mm thick dry layer SD | : | 0.02 m |
Capillary action water absorption coefficient W24 | : | 0.09 [kg/(m²·h0.5)] |
Adhesion to concrete | : | 2.40 N/mm² |
Resistance to the passage of vapour of a 0.10 mm thick dry layer SD | : | ISO 7783/2 |
Vapour diffusion resistance coefficient | : | ISO 7783/2 |
Change in colour after 1,000 hours exposure to a Weather-Ometer | : | according to ASTM G 155 cycle 1 |
Elongation at failure after 7 days at +23°C: | : | DIN 53504 |
Ultimate tensile strength after 7 days at +23°C: | : | DIN 53504 |
Wet abrasion | : | DIN 53778 |
Capillary action water absorption coefficient W24 | : | ISO 1062/3 |