General Specification
| Application | : | PVC | UPVC | Steel | Galvanized steel | Aluminum | Masonry surface |
| Application Method | : | Roller | Brush | Compressed air spray | Airless spray |
| Colour | : | White |
| Finish | : | Matte |
| Finishes | : | Matt |
| Material | : | Water-based acrylic anti-corrosion primer |
| Type | : | Metal (Primer), Primer |
Size
| Dry Film Thickness | : | 35μm - 45μm |
| Packing | : | 5L | 18L |
Technical
| Anti-corrosion property | : | Yes |
| Dilution | : | No, Use clean water if necessary | Brush / Roller – 5% | Spray – 15~20% |
| Drying time (at 25ºC) | : | Touch dry: 20 mins |
| Eco-friendly | : | Yes |
| Full Curing (at 25 ºC) | : | 7 days |
| Good adhesion | : | Yes |
| Overcoat Time (at 25ºC) | : | 4 hrs |
| Quick drying | : | Yes |
| Shelf Life | : | 24 months in sealed original packaging stored at room temperature and shaded place |
| Solid Content | : | >40% |
| Specific Gravity (at 20ºC) | : | >1.0 |
| Theoretical Coverage | : | 10.4 m2 /L/coat (35μm) | 6.90 m2 /L/coat (45μm) |
Certification
| Certification | : | CIC Green Product Certification |
| Test Standards | : | USEPA Method 24 | ASTM D5910-05 (2012) | CPSC-CH-C1001-09.3 | ISO 3856-1,4,5,7,3 : 1984 | ASTM D562-81 Procedure B | BS 3900 : Part C6 : 2000 | BS 3900 : C2 : 1994 | BS 3900 : C3 : 1990 | BS 3900 : Part E6 : 1992 | JIS K5660 : 2008 7.7 | JIS K5400 : 1990 |